Double Coated LiNiCoMnO2 Aluminum Foil For Li-Ion Pouch Cell Battery Cathode Materials

This electrode sheet is based on Aluminum foil coated by Lithium Nickel Manganese Cobalt Oxide in double side and is used as the cathode of Li-Ion battery -- 5 sheets /bag

SPECIFICATIONS

• Material:  LiNiCoMnO2  ( 5:2:3)
  
• Current collector (substrate): Aluminum foil ( 15 microns)
• Cathode material: Lithium Nickel Manganese Cobalt Oxide
• Double sides active material density: 242g/m²
• Active Material Weight: 9.642g
• Active Material Proportion in Powder: 94.2%
• Specific Capacity: 155 mAh/g
• Average Cycle Life: 500 Cycles @ 0.2C Charging/Discharging Rate
  
• Length: 241mm
• Width: 200mm
• Thickness: 103um +/- 5um
  Foil Thickness: 15um +/- 5um
  Coating Thickness: 88um +/- 10um (double side coated)
• Net Weight: 27.5g
• Double side coated
• Qty: 5 sheets/bag
• Note:  The electrode sheet shall be stored in a vacuum box, a vacuum oven or a glove box to avoid degradation